Product Description:Laser welding robot system is a laser diode (LD) as a heat source, locally implemented by non-contact heating laser, which has a non-contact, without changing the tip, the laser beam diameter is small. Some NA wave, reflow of parts, can only be installed after the adoption process, the use of local heating method to complete the assembly of the entire product
  • Technical Data
  • Applications White Paper
  • Related Products

    一、产品图片:

    二、产品参数:

    1. 激光波长:800~1100nm
    2. 光纤:SMA905/D80/QBH NA0.22
    3. 标准聚焦比例:1:1
    4. 视场范围:Φ3~20mm
    5. 照明波长:400~700nm
    6. 激光功率 < 500W
    7. 红外测温:100~600℃

    二极管激光器锡焊应用

    一:技术背景

    当今的电子装置已向多功能化,高集成化,小型化方向发展,以前的生产方式考虑比较多的制品的品质和实装技术的提高,但随着移动电话的小型化和多功能化以及3G手机的导入,小型化的趋势在加速,集成电路元件的引脚间距也从当初的1.0mm发展为0.8mm,0.65mm,0.5mm,而且现在以0.4mm,0.3mm都很为普遍(图一),并且部件之间的空间也越来越小。

    在使用以往对被焊工件进行焊接时,必须留有一定空间让烙铁头能伸入至被焊部位进行焊接,而且焊接过程烙铁头存在大量损耗,所以我们必须寻找新的焊接方式,在这状况下一种非接触式,细小直径加热方式的激光焊接系统应运而生。

    二:目的

    传统的焊接方式存在着烙铁头耗量大,且必须是接触式焊接等不足,新的直接二极管激光全自动锡焊弥补了传统焊接加工的不足。同时对于手机的CCD部件,LCD部件,手机的微型受话器,手携电脑的HDD部件,LCD部件以及微型马达,微型变压器等,还对应用液晶TV,高端数字相机,航空航天军工制造,高端汽车部件制造等领域领域的加工提供工艺支持(如图二)。

    三:原理和方法

    激光焊接机器人系统是以输出激光波长808nm的二极管激光器(LD)为热源,通过激光实行局部非接触加热,来完成整个产品的组装.(图三)

    激光锡焊工艺方法如下:

    1)选用的激光焊接系统重要的参数如下:激光输出波长:808nm激光输出最大功率:30-50W
    2).通过对系统控制单元的液晶触摸屏(图四)设定焊接的激光输出功率,激光照射时间,焊接温度曲线,以及送锡时间。
    3).利用系统同轴CCD摄像头与监视装置(图五),对被焊接工件进行定位。激光控制单元接收定位完成信号,开激光对焊接区域进行设定时间内的局部照射。

    四:方法实例

    下面通过一段视频来说明激光锡焊的工艺方法(图六)